反应方程式

azobisisobutyronitrile

lauryl methacrylate

N-vinyl-2-pyrrolidone

→

N-vinyl-2-pyrrolidone lauryl methacrylate

反应条件

后处理

1. 1
   其他The mixture was reacted at 60 to 70° C. for about 12 hours at nitrogen atmosphere

实验过程

The N-vinyl-2-pyrrolidone/lauryl methacrylate (6/94) copolymer was prepared in the following manner. In 100 parts of 0-grade Solvent L were placed 47 parts of lauryl methacrylate, 3 parts of N-vinyl-2-pyrrolidone and 0.2 parts of azobisisobutyronitrile (polymerization initiator). The mixture was reacted at 60 to 70° C. for about 12 hours at nitrogen atmosphere.