反应 #1365695

反应方程式

terephthaloyl chloride

water

terephthaloyl chloride

4,4′-diamino-2,2′-biphenyldisulfonic acid

sodium carbonate

→

desired polymer

收率 89.5%

4,4′-diamino-2,2′-biphenyldisulfonic Acid benzene-1,4-dicarbonyl Chloride

收率 89.5%

溶剂

chloroform

chloroform

chloroform

chloroform

ethanol

反应条件

后处理

1. 1
   其他Into a 1-L fluted round-bottom flask equipped with a mechanical stirring shaft
2. 2
   workup.DISSOLUTIONis dissolved
3. 3
   其他is obtained
4. 4
   其他is prepared
5. 5
   其他is also prepared
6. 6
   workup.STIRRINGThe reaction flask is stirred at high speed (800-1000 rpm)
7. 7
   workup.STIRRINGThe mixture is stirred for five minutes
8. 8
   其他resulting in an emulsion
9. 9
   workup.ADDITIONadded to the flask as quickly as possible
10. 10
    workup.STIRRINGThe reaction mixture is stirred at high speed at room temperature for 2-3 hours
11. 11
    workup.ADDITIONAt the end of this period the thickened gel-like solution is poured into large flask
12. 12
    过滤The resulting solid is filtered
13. 13
    其他dried in a vacuum oven

实验过程

Into a 1-L fluted round-bottom flask equipped with a mechanical stirring shaft, is placed 250 mL of deionized water and 7.95 g of sodium carbonate. The mixture is stirred until the carbonate salt is dissolved. Then, 7.64 g of 4,4′-diamino-2,2′-biphenyldisulfonic acid (DABS, 85%) is added and stirring is continued until a homogeneous solution is obtained. A solution containing 2.00 g of PEG 400 distearate surfactant dissolved in 100 mL of purified chloroform is prepared and set aside. Another solution containing 3.79 g of terephthaloyl chloride and 0.05 g of 1,5-benzenetricarbonyl trichloride dissolved in 100 mL of purified chloroform is also prepared. The reaction flask is stirred at high speed (800-1000 rpm), and the chloroform/surfactant solution is added quickly to the flask. The mixture is stirred for five minutes, resulting in an emulsion. Then, the chloroform solution containing the terephthaloyl chloride added to the flask as quickly as possible. The reaction mixture is stirred at high speed at room temperature for 2-3 hours. At the end of this period the thickened gel-like solution is poured into large flask containing 300 mL ethanol/900 mL acetone. The resulting solid is filtered and dried in a vacuum oven to provide 9.15 grams of the desired polymer as a fluff, light purple solid.