反应 #1106659

反应方程式

NaOH

MeOH

Maleic Anhydride

Phenyl Ethyl Norbornene

AIBN

→

MA PENB

溶剂

THF

THF

反应条件

后处理

1. 1
   workup.ADDITIONcharged to a reaction vessel
2. 2
   其他The solution was sparged with nitrogen for 10 min
3. 3
   其他to remove oxygen
4. 4
   workup.ADDITIONafter which the solution was diluted to 20 wt % with 148.04 g of THF
5. 5
   workup.ADDITIONwere mixed at 70° C. for 1 hr
6. 6
   workup.STIRRINGto stir for 3 hr at 70° C.
7. 7
   温度was cooled to room temperature
8. 8
   workup.ADDITIONThe reaction mixture was treated with conc. HClaq for protonation
9. 9
   洗涤washed three times
10. 10
    其他to remove residual salts and acid
11. 11
    其他The organic phase was separated
12. 12
    浓缩concentrated in vacuo
13. 13
    workup.DISSOLUTIONredissolved in THE
14. 14
    其他to form an approximately 20 wt % copolymer solution
15. 15
    其他the copolymer was precipitated
16. 16
    workup.ADDITIONby adding the THF solution to hexane (20 fold excess)
17. 17
    其他The copolymer was separated by filtration
18. 18
    其他dried in a vacuum oven at 80° C. for 16 hr

实验过程

Maleic Anhydride (MA, 14.7 g, 150 mmol), Phenyl Ethyl Norbornene (PENB, 29.7 g, 150 mmol) and AIBN (2.5 g, 15.0 mmol) was dissolved in THF (27.1 g) and charged to a reaction vessel. The solution was sparged with nitrogen for 10 min to remove oxygen and then heated to 60° C. The mixture was allowed to stir at 60° C. for 24 hr, after which the solution was diluted to 20 wt % with 148.04 g of THF. The resulting solution was added to the suspension of NaOH (6.6 g, 165 mmol), MeOH (24.0 g, 750 mmol) and THF (24.0 g) which were mixed at 70° C. for 1 hr. The mixture was allowed to stir for 3 hr at 70° C. and then was cooled to room temperature. The reaction mixture was treated with conc. HClaq for protonation, and then washed three times to remove residual salts and acid. The organic phase was separated and then concentrated in vacuo, redissolved in THE to form an approximately 20 wt % copolymer solution and then the copolymer was precipitated by adding the THF solution to hexane (20 fold excess). The copolymer was separated by filtration and dried in a vacuum oven at 80° C. for 16 hr. Approximately, 28.7 g (58%) of the Ring-opening polymer of MA/PENB with MeOH was isolated (GPC Mw=6,400 Mn=3,500).