反应 #1006000

反应方程式

methanol

acrylamide

benzoyl peroxide

isooctyl acrylate

→

Isooctylacrylate Acrylamide

溶剂

ethyl acetate

ethyl acetate methanol

—

solids

ethyl acetate

反应条件

后处理

1. 1
   其他The solution was purged for thirty five seconds with nitrogen at a flow rate of one liter per minute
2. 2
   其他The bottle was sealed
3. 3
   workup.WAITplaced in a rotating water bath at 55° C. for twenty-four hours
4. 4
   其他polymerization

实验过程

To a 114 gram narrow-mouth glass bottle were added: 18.6 g isooctyl acrylate, 1.4 g acrylamide, 0.04 g benzoyl peroxide, 27.0 g ethyl acetate and 3.0 g methanol. The solution was purged for thirty five seconds with nitrogen at a flow rate of one liter per minute. The bottle was sealed and placed in a rotating water bath at 55° C. for twenty-four hours to effect essentially complete polymerization. The polymer was diluted with ethyl acetate/methanol (90/10) to 23.2 percent solids and had a measured inherent viscosity of 1.26 dl/g in ethyl acetate.

来源