Реакция #56350

Уравнение реакции

ethyl acrylate

boron trifluoride

allyl acrylate

azobis(isobutyronitrile)

ethylene

ethylene

maleic anhydride

→

Ethylene/Ethyl Acrylate Allyl Acrylate Maleic Anhydride

Растворители

methylene chloride

acetone

Условия реакции

Обработка

1. 1
   workup.ADDITIONwas charged under nitrogen with 4000 ml
2. 2
   ДругоеIt was then sealed
3. 3
   ДругоеThe subsequent copolymerization at 25° C.
4. 4
   Другоеabout two hours
5. 5
   ДругоеThe reaction was quenched by addition of one liter of diethyl ether
6. 6
   ДругоеVolatiles were removed by steam-stripping in a well-ventilated hood
7. 7
   ДругоеThe terpolymer thereby obtained
8. 8
   Другоеprecipitated in water in a blender
9. 9
   Другоеoven-dried

Методика

A 7.57-liter stirred autoclave was charged under nitrogen with 4000 ml. of methylene chloride, 400 grams of ethyl acrylate, 20 grams of maleic anhydride, 1.2 grams of allyl acrylate, and 1.0 gram of azobis(isobutyronitrile). It was then sealed, charged with 300 grams of boron trifluoride, and pressured to 21 kg./sq. cm. with ethylene. The subsequent copolymerization at 25° C. was continued until pressure measurement indicated that ethylene uptake had ceased (about two hours later). The reaction was quenched by addition of one liter of diethyl ether. Volatiles were removed by steam-stripping in a well-ventilated hood. The terpolymer thereby obtained was dissolved in acetone, precipitated in water in a blender, and oven-dried. Yield: 415 grams.