1-dodecanol

stannous octoate

→

ε-CAPROLACTONE L-LACTIDE

Условия реакции

Обработка

1. 1
   ДругоеThe copolymer was dried under vacuum (0.1mm Hg) at 110° C. for about 16 hours
2. 2
   Другоеto remove any unreacted monomer
3. 3
   Другоеat 25° C
4. 4
   Другоеat room temperature

Методика

The procedure in Example 1 was substantially repeated, except that 13.6 mL of 1-dodecanol instead of 4.00 mL of glycerol and 0.12 mL (40 μmol) instead of 0.10 mL of stannous octoate solution were used. The copolymer was dried under vacuum (0.1mm Hg) at 110° C. for about 16 hours to remove any unreacted monomer. The copolymer had an inherent viscosity of 0.15 dL/g in HFIP at 25° C. The copolymer was viscous liquid at room temperature. The molar ratio of PC.L/PLA was found to be 51.5/48.5 by proton NMR.