반응 #487501

반응 방정식

zirconium hydroxide

zirconium

phosphoric acid

phosphorus

→

zirconium phosphate

용매

water

반응 조건

후처리

1. 1
   기타Catalyst preparation
2. 2
   기타A zirconium phosphate based catalyst was prepared by a co-precipitation method
3. 3
   기타to remove water
4. 4
   기타a paste was obtained
5. 5
   기타The resulting paste was then dried in an oven at 100° C. overnight (about 12-18 hours)
6. 6
   기타to remove the bulk of any remaining water
7. 7
   기타to provide a powder

실험 절차

Catalyst preparation. A zirconium phosphate based catalyst was prepared by a co-precipitation method. A solution of zirconium hydroxide (Zr(OH)4) as a zirconium precursor was dissolved in deionized water. To this solution, a stoichiometric amount of phosphoric acid as a phosphorus precursor was added. The resulting mixture was heated at 80° C. for 2 hours to remove water, and a paste was obtained. The resulting paste was then dried in an oven at 100° C. overnight (about 12-18 hours) to remove the bulk of any remaining water, and to provide a powder. The powder was then calcined at 350° C. for 2 hours to obtain powdered zirconium phosphate.