반응 #417902

반응 방정식

p-tert-Butoxystyrene

cyclohexyl acrylate

2,2′-azobisisobutyronitrile

→

p-tert-butoxystyrene cyclohexyl acrylate

용매

isopropanol

methanol

반응 조건

후처리

1. 1
   기타a polymerization reaction at 75° C. for 6 hours
2. 2
   온도The reaction solution was cooled
3. 3
   여과The precipitated crystal was collected by filtration
4. 4
   세척washed with methanol
5. 5
   기타dried under reduced pressure

실험 절차

p-tert-Butoxystyrene (176.3 g (1.0 mol)) and 16.2 g (0.105 mol) of cyclohexyl acrylate were dissolved in 250 ml of isopropanol, and in a nitrogen stream, 2,2′-azobisisobutyronitrile was added. The mixture was allowed to undergo a polymerization reaction at 75° C. for 6 hours. The reaction solution was cooled and then poured in 5,000 ml of methanol for crystallization. The precipitated crystal was collected by filtration, washed with methanol and dried under reduced pressure to obtain 172.5 g of poly(p-tert-butoxystyrene/cyclohexyl acrylate) as white powder crystal. The component ratio between p-tert-butoxystyrene unit and cyclohexyl acrylate unit in the obtained resin was found to be about 90:10 from 1HNMR and 13CNMR measurements. Also, the results of GPC measurement using polystyrene as a standard were Mw of about 20,600 and Mw/Mn of 1.55.

출처