반응 #2419

반응 방정식

acetone

oleum

4,4'-diamino-6-carbamoyl benzanilide

NH4OH

→

4,4'-diamino-6-cyanobenzanilide

용매

ethanol

반응 조건

후처리

1. 1
   온도already cooled down to -5° to 0° C
2. 2
   세척The solution was sufficiently washed
3. 3
   기타to remove salt
4. 4
   여과by filtering
5. 5
   세척washed with a small amount of warm ethanol
6. 6
   기타dried in a vacuum oven at 80° C
7. 7
   workup.ADDITIONThe dried reactant which was mixed with by-products
8. 8
   추출was extracted by soxlet
9. 9
   workup.ADDITIONtreated with the activated carbon
10. 10
    workup.ADDITIONethanol was added
11. 11
    기타to recrystallize in the mixture solvent (acetone:ethanol=1:1)
12. 12
    여과The light yellow-scalelike crystal was filtered
13. 13
    기타dried in a vacuum oven at 80° C
14. 14
    추출The light yellow-scalelike crystal was extracted again by soxlet with acetone
15. 15
    workup.ADDITIONtreated with the activated carbon
16. 16
    기타And then the white-scalelike crystal obtained
17. 17
    건조was dried in a vacuum oven at 80° C. (40 g of the raw material
18. 18
    기타was obtained
19. 19
    기타thereof was 250° to 251° C.

실험 절차

350 ml of oleum (30% by weight) was cooled down below 0° C. using an ice bath, 99.6 g (0.368 mol) of 4,4'-diamino-6-carbamoyl benzanilide in a powder form was added below 5° C. with stirring. The stirring was continued to the next day, and the solution was neutralized by adding 1100 ml of NH4OH (28% by weight) already cooled down to -5° to 0° C. The solution was sufficiently washed to remove salt by filtering and washed with a small amount of warm ethanol and then dried in a vacuum oven at 80° C. The dried reactant which was mixed with by-products was extracted by soxlet and treated with the activated carbon and then ethanol was added to recrystallize in the mixture solvent (acetone:ethanol=1:1). The light yellow-scalelike crystal was filtered and dried in a vacuum oven at 80° C. The light yellow-scalelike crystal was extracted again by soxlet with acetone and treated with the activated carbon. And then the white-scalelike crystal obtained by recrystalling in the mixture solvent (acetone:ethanol=1:1) was dried in a vacuum oven at 80° C. (40 g of the raw material was obtained and the boiling point thereof was 250° to 251° C.).

출처