반응 #171128

반응 방정식

acrylic acid

α-methylene-γ-butyrolactone

n-butyl acrylate

water

water

sodium dodecyl sulfate

sodium hydroxide

sodium persulfate

sodium dodecyl sulfate

→

α-methylene-γ-butyrolactone n-butyl acrylate acrylic acid

반응 조건

후처리

1. 1
   기타To a 100 mL round bottom flask equipped with a magnetic stir bar
2. 2
   workup.ADDITIONwas added via syringe pump over 115 minutes
3. 3
   workup.ADDITIONAfter 10 minutes of monomer mixture addition
4. 4
   workup.ADDITIONwas added via syringe pump over 115 minutes
5. 5
   workup.ADDITIONAfter both the monomer and aqueous mixtures were added completely
6. 6
   온도after which the reaction was cooled to room temperature
7. 7
   기타dried under vacuum under vacuum at 90° C. overnight
8. 8
   기타Size exclusion chromatography yielded a monomodal peak with a weight average molecular weight of 296 kDa
9. 9
   기타at approximately 21° C.

실험 절차

To a 100 mL round bottom flask equipped with a magnetic stir bar was added 8.819 g (0.490 mol) water and 0.116 g (4.02×10−4 mol) sodium dodecyl sulfate (20% aqueous solution). The mixture was heated under flowing nitrogen to 73° C., at which time a monomer mixture consisting of 2.102 g (2.14×10−2 mol) α-methylene-γ-butyrolactone, 2.102 g n-butyl acrylate (1.64×10−2 mol) and 0.220 g (3.66×10−3 mol) acrylic acid was added via syringe pump over 115 minutes. After 10 minutes of monomer mixture addition, an aqueous mixture consisting of 16.711 g (0.928 mol) water, 0.267 g (9.26×10−4 mol) sodium dodecyl sulfate (20% aqueous solution), 0.026 g (1.09×10−4 mol) sodium persulfate, and 0.033 g of a 20% aqueous sodium hydroxide solution was added via syringe pump over 115 minutes. After both the monomer and aqueous mixtures were added completely, the emulsion was allowed to stir for an additional 60 minutes, after which the reaction was cooled to room temperature and dried under vacuum under vacuum at 90° C. overnight. Size exclusion chromatography yielded a monomodal peak with a weight average molecular weight of 296 kDa and a polydispersity of 2.84, relative to polystyrene standards. Differential scanning calorimetry showed a single first order transition at approximately 21° C.