반응 #1536835

반응 방정식

ε-caprolactone

p-dioxanone

glycerol

stannous octoate

→

ε-CAPROLACTONE p-DIOXANONE

용매

toluene

반응 조건

후처리

1. 1
   기타A flame dried
2. 2
   기타The flask was fitted with a flame
3. 3
   기타dried mechanical stirrer
4. 4
   기타The flask was purged with nitrogen three times
5. 5
   온도maintained at this temperature for about 24 hours
6. 6
   온도The reaction mixture was then cooled to 110° C.
7. 7
   온도maintained at this temperature for 24 hours
8. 8
   기타The copolymer was dried under vacuum (0.1 mm Hg) at 80° C. for about 32 hours
9. 9
   기타to remove any unreacted monomer
10. 10
    기타at 25° C
11. 11
    기타at room temperature

실험 절차

A flame dried, 250 mL, round bottom single neck flask was charged with 57.1 grams (0.50 mole) of ε-caprolactone, 51.0 grams (0.50 mole) of p-dioxanone, 4.00 mL (55 mmol) of distilled glycerol, and 0.12 mL (40 μmol) of a 0.33M stannous octoate solution in toluene. The flask was fitted with a flame dried mechanical stirrer. The flask was purged with nitrogen three times before venting with nitrogen. The reaction mixture was heated to 140° C. and maintained at this temperature for about 24 hours. The reaction mixture was then cooled to 110° C. and maintained at this temperature for 24 hours. The copolymer was dried under vacuum (0.1 mm Hg) at 80° C. for about 32 hours to remove any unreacted monomer. The copolymer had an inherent viscosity of 0.14 dL/g in HFIP at 25° C. The copolymer was a liquid at room temperature. The molar ratio of PCL/PDS was found to be 53.2/46.8 by proton NMR.

출처