반응 #1106660

반응 방정식

NaOH

MeOH

Maleic Anhydride

Phenyl Ethyl Norbornene

AIBN

→

MA PENB

용매

THF

EtOAc

반응 조건

후처리

1. 1
   workup.ADDITIONcharged to a reaction vessel
2. 2
   기타The solution was sparged with nitrogen for 10 min
3. 3
   기타to remove oxygen
4. 4
   농축The reaction mixture was concentrated in vacuo
5. 5
   workup.DISSOLUTIONredissolved in THF (20 wt %)
6. 6
   workup.ADDITIONwere mixed at 70° C. for 1 hr
7. 7
   workup.STIRRINGto stir for 3 hr at 70° C.
8. 8
   온도was cooled to room temperature
9. 9
   workup.ADDITIONThe reaction mixture was treated with conc. HClaq for protonation
10. 10
    세척washed three times
11. 11
    기타to remove residual salts and acid
12. 12
    기타The organic phase was separated
13. 13
    농축concentrated in vacuo
14. 14
    workup.DISSOLUTIONredissolved in THF
15. 15
    기타to form an approximately 20 wt % copolymer solution
16. 16
    기타the copolymer was precipitated
17. 17
    workup.ADDITIONby adding the THF solution to hexane (20 fold excess)
18. 18
    기타The copolymer was separated by filtration
19. 19
    기타dried in a vacuum oven at 80° C. for 16 hr

실험 절차

Maleic Anhydride (MA, 14.7 g, 150 mmol), Phenyl Ethyl Norbornene (PENB, 29.7 g, 150 mmol) and AIBN (2.5 g, 15.0 mmol) was dissolved in EtOAc (27.1 g) and charged to a reaction vessel. The solution was sparged with nitrogen for 10 min to remove oxygen and then heated to 60° C. The mixture was allowed to stir at 60° C. for 24 hr. The reaction mixture was concentrated in vacuo and redissolved in THF (20 wt %). The resulting solution was added to the suspension of NaOH (6.6 g, 165 mmol), MeOH (24.0 g, 750 mmol) and THF (24.0 g) which were mixed at 70° C. for 1 hr. The mixture was allowed to stir for 3 hr at 70° C. and then was cooled to room temperature. The reaction mixture was treated with conc. HClaq for protonation, and then washed three times to remove residual salts and acid. The organic phase was separated and then concentrated in vacuo, redissolved in THF to form an approximately 20 wt % copolymer solution and then the copolymer was precipitated by adding the THF solution to hexane (20 fold excess). The copolymer was separated by filtration and dried in a vacuum oven at 80° C. for 16 hr. Approximately, 30.4 g (61%) of the Ring-opening polymer of MA/PENB with MeOH was isolated (GPC Mw=9,700 Mn=5,300).