A solution of 985.94 grams (11.715 mole) 1-hexene and 58.24 grams (0.4831 mole) 1,7-octadiene (molar charge ratio 96:4) in 450 grams of heptane was polymerized with Et2AlCl (13.5 millimoles) and AATiCl3 (6.97 millimoles) at 25° C. for 20 hours. During the course of the reaction, hydrogen was bubbled through the reaction mixture. The conversion of the polymer was 62 percent, inherent viscosity was 1.6 dl/gram. The composition of monomers in the copolymer was 97.8:2.2 mole ratio from NMR analysis.