反応 #3849

反応方程式

ethylene oxide

ethylene oxide

ethylene oxide

ethylene

ethylene oxide

ethylene oxide

neononanoic acid

ethylene oxide

ethylene oxide

ethylene oxide

→

ethylene glycol mononeononanoate

溶媒

反応条件

後処理

1. 1
   温度heater, cooling coils, automatic temperature controller
2. 2
   その他a gaseous N2 purge of the reactor
3. 3
   workup.ADDITIONis introduced
4. 4
   その他to remove both oxygen and water
5. 5
   温度With continued N2 purging its temperature of the neo acid/catalyst solution is gradually raised to 150° C
6. 6
   その他the N2 purge
7. 7
   その他the reactor vents are sealed
8. 8
   workup.ADDITIONEthylene oxide is then slowly added to the reactor until a pressure of 60 psig
9. 9
   その他is obtained
10. 10
    その他As the reaction between the neo acid
11. 11
    workup.ADDITIONis again slowly charged to the reactor until a pressure of 60 psig
12. 12
    その他is obtained
13. 13
    その他is obtained
14. 14
    workup.ADDITIONhas been added to the reaction
15. 15
    workup.WAITis about 55 minutes
16. 16
    その他a gaseous nitrogen purge
17. 17
    workup.ADDITIONis introduced
18. 18
    温度the reaction product is cooled to room temperature

実験手順

To a one liter stainless steel autoclave, equipped with a mechanical stirrer, heater, cooling coils, automatic temperature controller, and a tared ethylene oxide cylinder, in a series of runs is added 500 grams neononanoic acid and 2.0 g of the selected catalyst. The reactor is heated to approximately 100° C. and a gaseous N2 purge of the reactor is introduced to remove both oxygen and water. With continued N2 purging its temperature of the neo acid/catalyst solution is gradually raised to 150° C. Upon reaching temperature, the N2 purge is stopped and the reactor vents are sealed. Ethylene oxide is then slowly added to the reactor until a pressure of 60 psig is obtained. The ethylene oxide flow is then stopped. As the reaction between the neo acid and the ethylene proceeds, the pressure of the reactor vessel will slowly decrease. When the pressure reaches 20 psig, ethylene oxide is again slowly charged to the reactor until a pressure of 60 psig is obtained. The ethylene oxide flow is then decreased to the point where a steady reactor pressure of 60 psig is obtained. The addition of ethylene oxide continues until the desired quantity of ethylene oxide has been added to the reaction. The flow of ethylene oxide is then stopped. The reaction mixture is stirred for an additional 20 minutes, until the reactor pressure decreases to 15 psig. Total reaction time, from the start of ethylene oxide addition is about 55 minutes. The reactor is then vented, a gaseous nitrogen purge is introduced, and the reaction product is cooled to room temperature. The crude ethylene glycol mononeononanoate product mixture thereby obtained was characterized by gas chromatography and found to have the following characteristics: