反応 #2146714

反応方程式

diethyl carbonate

2,2′-azobis(isobutyronitrile)

methyl methacrylate

3-ethyl-3-oxetanylmethyl methacrylate

3,4-epoxycyclohexylmethyl acrylate

ethylene carbonate

2,2′-azobis(isobutyronitrile)

→

ethylene carbonate diethyl carbonate

反応条件

後処理

1. 1
   その他equipped with a refluxing condenser
2. 2
   workup.ADDITIONmixed for 30 minutes while nitrogen gas
3. 3
   workup.ADDITIONwas introduced into the flask
4. 4
   その他radical polymerization
5. 5
   その他The resulting reaction mixture
6. 6
   温度was cooled to 40° C
7. 7
   温度the resulting mixture was again heated to 70° C.
8. 8
   その他polymerization at the temperature for another 8 hours
9. 9
   その他Then the resulting reaction mixture
10. 10
    温度was cooled to 40° C.

実験手順

60.0 g of methyl methacrylate, 16.0 g of 3-ethyl-3-oxetanylmethyl methacrylate, 4.0 g of 3,4-epoxycyclohexylmethyl acrylate, 226.6 g of ethylene carbonate and 0.15 g 2,2′-azobis(isobutyronitrile) were placed in a 500 mL capacity three-necked flask equipped with a refluxing condenser and stirred and mixed for 30 minutes while nitrogen gas was introduced into the flask. Then the resulting mixture was heated to 70° C. and radical polymerization was carried out over 8 hours at the temperature. The resulting reaction mixture was cooled to 40° C. 226.6 g of diethyl carbonate and 0.15 g of 2,2′-azobis(isobutyronitrile) were added to the reaction mixture and the resulting mixture was again heated to 70° C. to carry out radical polymerization at the temperature for another 8 hours. Then the resulting reaction mixture was cooled to 40° C. to obtain a solution of a polymer in a concentration of 15% by weight in a solvent of ethylene carbonate/diethyl carbonate mixture.