反応 #1702026

反応方程式

t-BHQ

bis(methyl salicyl) carbonate

BPA

sodium hydroxide

BPA

BPA

t-BHQ

BMSC

p-cumylphenol

BMSC BPA

t-BHQ

→

t-BHQ BPA

溶媒

tetramethylammonium hydroxide

反応条件

後処理

1. 1
   その他A stainless steel tank reactor equipped with stirrers
2. 2
   その他The reactor was then evacuated
3. 3
   その他purged with nitrogen three times
4. 4
   その他to remove residual oxygen
5. 5
   温度30 minutes from the start of heating
6. 6
   その他the molten reaction mixture
7. 7
   その他was fed through a 170° C.
8. 8
   温度heated feed-line into an extruder at a rate of 13.5 kg/h
9. 9
   その他The extruder was equipped with five forward vacuum vents and one back-vent
10. 10
    その他The methyl salicylate by-product was removed via devolatilization through the vacuum vents
11. 11
    その他were set at a temperature of 300° C.
12. 12
    その他was set at a temperature of 310° C

実験手順

Melt Oligomerization-Reactive Extrusion: A 50 mole percent t-BHQ/BPA copolycarbonate was prepared via melt oligomerization of t-BHQ and BPA with bis(methyl salicyl) carbonate (BMSC) followed by a reactive extrusion process to achieve high molecular weight BHQ/BPA copolycarbonate. A stainless steel tank reactor equipped with stirrers was charged with about 10953 g of BPA, 7975.5 g of t-BHQ, 32187.6 g of BMSC and 252.8 g of p-cumylphenol (PCP) in a molar ratio of BMSC/BPA to t-BHQ of about 1:1.0155. An aqueous catalyst solution of tetramethylammonium hydroxide (1650 microliter (μl), TMAH) and sodium hydroxide (NaOH) were added to the reactor. The reactor was then evacuated and purged with nitrogen three times to remove residual oxygen and then held at a constant vacuum pressure of 800 mbar. The reactor was then heated to 170° C. in order to melt and oligomerize the reactants. After approximately 4 hours and 30 minutes from the start of heating, the reactor was pressurized with nitrogen to a constant overpressure of 1.4 bar, and the molten reaction mixture was fed through a 170° C. heated feed-line into an extruder at a rate of 13.5 kg/h. The extruder employed was a Werner & Pfleiderer ZSK25WLE 25 mm, 13-barrel, twin-screw extruder with a length/diameter ratio (L/D) of 59. The feed inlet communicating with the extruder comprised a flash-valve to prevent boiling of the molten mixture. The extruder was equipped with five forward vacuum vents and one back-vent. The vacuum pressure of the back-vent was about 13 mbar. The vacuum pressure of the first forward vent was about 14 mbar and the vacuum pressure of the final four forward vents was less than about 1 mbar. The methyl salicylate by-product was removed via devolatilization through the vacuum vents. All the extruder barrels were set at a temperature of 300° C. and the extruder die head was set at a temperature of 310° C. The reaction mixture was reactively extruded at a screw speed of 300 rpm.