Reacción #3149

ord-889d3fb76dc4464094f72ea8e4bc1474

Ecuación de reacción

C=CC(N)=O
acrylamide
[Cl-]
chloride
C=CC(=O)OCC
ethyl acrylate
O=C(O)CN(CCN(CC(=O)O)CC(=O)O)CC(=O)O
EDTA
CC(C)(N=NC(C)(C)C1=NCCN1)C1=NCCN1.Cl.Cl
VA-044
→
C=CC(N)=O
AMD
C=CC(=O)OCC.CCl
MeCl EA

Reactantes

—
aqueous solution
C=CC(N)=O
acrylamide
[Cl-]
chloride
C=CC(=O)OCC
ethyl acrylate
O=C(O)CN(CCN(CC(=O)O)CC(=O)O)CC(=O)O
EDTA
CC(C)(N=NC(C)(C)C1=NCCN1)C1=NCCN1.Cl.Cl
VA-044

Reactivos

Ninguno

Disolventes

O
water

Condiciones de reacción

Condiciones detalladas
See reaction.notes.procedure_details.

Tratamiento posterior

  1. 1
    OtroThe solution was sparged with nitrogen gas
  2. 2
    OtroThe nitrogen sparge
  3. 3
    Otropurge
  4. 4
    Otropolymerization
  5. 5
    Temperaturaby raising the temperature of the solution to 44° C
  6. 6
    workup.STIRRINGStirring
  7. 7
    Temperaturaheating
  8. 8
    workup.WAITwere continued for about 21 hours

Procedimiento

A 10% solution of poly(AMD/DMAEA.MeCl/EA) was prepared as follows: 13.87 parts of 53.58% aqueous acrylamide (AMD), 25.31 parts of a 80% aqueous solution of ethacryloxyethyltrimethylammonium chloride (DMAEA.MeCl), 2.33 parts of ethyl acrylate (EA), 0.3 part EDTA, 258.16 parts of deionized water and 0.030 parts of VA-044 were added to a suitable glass vessel. The solution was sparged with nitrogen gas and stirred for about one hour at ambient temperature. The nitrogen sparge was changed to a nitrogen purge, and polymerization was initiated thermally by raising the temperature of the solution to 44° C. Stirring and heating were continued for about 21 hours to give a clear, viscous solution of poly(AMD/DMAEA.MeCl/EA) having a standard viscosity of about 2.0 centipoise.

Fuente

DOI: 10.6084/m9.figshare.5104873.v1Patente: US05733462uspto-grants-1998_03