Reaktion #941407

Reaktionsgleichung

ammonium persulphate

sodium

methacrylic acid ethylene oxide

styrene

methacrylic acid

butyl acrylate

ammonium persulphate

→

styrene-methacrylic acid butyl acrylate sodium

methacrylic acid ethylene oxide

Lösungsmittel

water

Reaktionsbedingungen

Aufarbeitung

1. 1
   SonstigeTo a reaction vessel equipped with a stirrer
2. 2
   Sonstigeto obtain a white emulsion
3. 3
   TemperaturThe white emulsion was heated
4. 4
   workup.WAITthe reaction was performed for 5 hours
5. 5
   workup.WAITthe reaction mixture was matured at 75° C. for 5 hours

Vorschrift

To a reaction vessel equipped with a stirrer and a thermometer, 683 parts of water, 11 parts of sodium salt of the sulfuric acid ester of methacrylic acid ethylene oxide adduct (ELEMINOL RS-30, manufactured by Sanyo Chemical Industries, Ltd.), 83 parts of styrene, 83 parts of methacrylic acid, 110 parts of butyl acrylate, and 1 part of ammonium persulphate were poured and stirred at 400 rpm for 15 minutes to obtain a white emulsion. The white emulsion was heated, the temperature in the system was raised to 75° C., and the reaction was performed for 5 hours. Next, 30 parts of an aqueous solution of 1% ammonium persulphate was further added, and the reaction mixture was matured at 75° C. for 5 hours to obtain an aqueous dispersion liquid of a vinyl resin (copolymer of styrene-methacrylic acid-butyl acrylate-sodium salt of the sulfuric acid ester of methacrylic acid ethylene oxide adduct) [particulate emulsion 1]. The volume average particle diameter of the [particulate emulsion 1] measured by LA-920 was 105 nm. After drying a part of [particulate emulsion 1] and isolating the resin, the glass transition temperature (Tg) of the resin was 59° C. and the mass average molecular mass was 150,000.

Quelle