Reaktion #529784

Reaktionsgleichung

p-vinylphenol

p-toluenesulfonic acid

water

water

water

ethylvinyl ether

→

poly (p-vinylphenol)

Lösungsmittel

1,4-dioxane

1,4-dioxane

Reaktionsbedingungen

Aufarbeitung

1. 1
   SonstigeInto a 500 ml four-necked flask purged with nitrogen
2. 2
   workup.ADDITIONwere charged 25 g of poly (p-vinylphenol) ["VP-5000" manufactured by Nippon Soda K.K.]
3. 3
   Sonstigereaction
4. 4
   Sonstigeseparated by filtration
5. 5
   Sonstigeto obtain a white wet cake
6. 6
   SonstigeThe resulting mixture was separated by filtration
7. 7
   SonstigeThe wet cake thus obtained
8. 8
   Waschenwas washed
9. 9
   Filtrationby being filtered
10. 10
    Sonstigeto obtain a wet cake
11. 11
    SonstigeThe resulting white wet cake was dried under reduced pressure

Vorschrift

Into a 500 ml four-necked flask purged with nitrogen were charged 25 g of poly (p-vinylphenol) ["VP-5000" manufactured by Nippon Soda K.K.] having a weight average molecular weight (Mw) of 8400 and a dispersion degree (Mw/Mn) of 1.19 (208 mmol as p-vinylphenol unit) and 0.024 g (0.125 mmol) of p-toluenesulfonic acid, and they were dissolved in 250 g of 1,4-dioxane. To this solution was added dropwise 9.0 g (125 mmol) of ethylvinyl ether, and then reaction was carried out for 5 hours at 25° C. This reaction solution was added dropwise into 1500 ml of ion-exchanged water, then separated by filtration to obtain a white wet cake. This wet cake was dissolved again in 200 g of 1,4-dioxane, and the resulting solution was added dropwise into 1500 ml of ion-exchanged water. The resulting mixture was separated by filtration. The wet cake thus obtained was washed by being stirred with 600 g of ion-exchanged water, followed by being filtered to obtain a wet cake. The washing operation with this ion-exchanged water was further repeated twice. The resulting white wet cake was dried under reduced pressure to obtain a resin in which the hydroxyl group of poly (p-vinylphenol) was partially 1-ethoxyethyl etherized. This resin was analyzed by 1H-NMR to find that 40% of the hydroxyl group was protected by a 1-ethoxylethyl group. This resin has a weight average molecular weight of 12300 and a dispersion degree of 1.23.