Reaktion #324373

Reaktionsgleichung

ethylene glycol monoethyl ether acetate

V-601

hexane

→

4-acetoxystyrene t-butyl methacrylate benzyl methacrylate

Reaktionsbedingungen

Aufarbeitung

1. 1
   Temperaturwas heated until the internal temperature of the flask
2. 2
   Sonstigebecame 80° C
3. 3
   workup.ADDITIONwas added
4. 4
   workup.ADDITIONSubsequently, the above monomer mixture solution was dropped into this solution over a period of six hours
5. 5
   TemperaturAfter the completion of the dropping, the mixture was further heated
6. 6
   workup.STIRRINGagitated for two hours
7. 7
   SonstigeThereafter, the reaction liquid
8. 8
   SonstigeAfter the cooling, the reaction liquid
9. 9
   Sonstigeprecipitating a polymer
10. 10
    FiltrationThe polymer solid was collected by filtration
11. 11
    workup.DISSOLUTIONdissolved in 500 g of acetone
12. 12
    workup.ADDITIONThis solution was dropped once more into three liters of hexane
13. 13
    Filtrationthe thus obtained solid was collected by filtration
14. 14
    Sonstigedried in vacuum

Vorschrift

The 2-liter flask charged with 600 g of ethylene glycol monoethyl ether acetate was heated until the internal temperature of the flask became 80° C. Then, 2.30 g (0.01 mol) of polymerization initiator V-601 was added thereto and agitated for five minutes. Subsequently, the above monomer mixture solution was dropped into this solution over a period of six hours. After the completion of the dropping, the mixture was further heated and agitated for two hours. Thereafter, the reaction liquid was cooled to room temperature. After the cooling, the reaction liquid was dropped into three liters of hexane, thereby precipitating a polymer. The polymer solid was collected by filtration and dissolved in 500 g of acetone. This solution was dropped once more into three liters of hexane, and the thus obtained solid was collected by filtration and dried in vacuum. Thus, 151 g of poly(4-acetoxystyrene/t-butyl methacrylate/benzyl methacrylate) was obtained.