تفاعل #947023

معادلة التفاعل

neodymium

1,4-butanediol

neodymium

butanediol

DIBAH

allyl bromide

1,4-butanediol

butadiene

diisobutylaluminum hydride

→

isoprene butadiene

المردود 87.0%

المذيبات

hexane

hexane

hexane

ظروف التفاعل

المعالجة

1. 1
   workup.DISSOLUTIONgradually dissolved
2. 2
   workup.STIRRINGAfter one hour of stirring
3. 3
   workup.ADDITIONwas added to the reactor
4. 4
   workup.ADDITIONwas added
5. 5
   درجة الحرارةto warm up to ambient (and above) temperature
6. 6
   درجة الحرارةby heating at 65° C. for ninety minutes
7. 7
   أخرىThe catalyst prepared
8. 8
   درجة الحرارةThe aged catalyst was then cooled

الإجراء التجريبي

In this experiment, an isoprene-butadiene copolymer was synthesized using an alcohol modified neodymium catalyst system modified with 1,4-butanediol. In this procedure, a one gallon (3.78 liter) reactor was charged with 1,093 grams of hexane containing 81.9 grams of butadiene and 663 grams of 1.2 molar diisobutylaluminum hydride (DIBAH) in hexane (i.e., 25% weight percent DIBAH). To this solution was then added 6.78 grams of 1,4-butanediol with stirring and with temperatures maintained at 20° C. The suspension of the butanediol gradually dissolved upon reacting with the DIBAH. After one hour of stirring, 105.4 grams of a 10.3% neodymium solution (neodymium neodecanoate), diluted with 165 grams of hexane, was added to the reactor. The solution was stirred for another thirty minutes after which time 19.1 grams of allyl bromide was added. The cooling was stopped and the mixture allowed to warm up to ambient (and above) temperature. After the exotherm subsided, the catalyst solution was aged by heating at 65° C. for ninety minutes. The catalyst prepared had a [butanediol-DIBAH]-ND-allyl bromide-butadiene molar component ratio of [1-16]-1-2-20, respectively, and a concentration of 0.025 molarity with respect to the neodymium. The aged catalyst was then cooled and stored in a dry container under nitrogen.

المصدر