تفاعل #657250

معادلة التفاعل

styrene

butyl acrylate

1-dodecanethiol

→

Styrene n-Butyl Acrylate

المذيبات

water

ظروف التفاعل

المعالجة

1. 1
   أخرىSeparately the monomer emulsion was prepared in the following manner
2. 2
   أخرىto form an emulsion
3. 3
   workup.ADDITIONcontaining the aqueous surfactant phase at 80° C.
4. 4
   أخرىto form the “seeds”
5. 5
   أخرىwhile being purged with nitrogen
6. 6
   workup.ADDITIONThe initiator solution was then slowly charged into the reactor and after 10 minutes the rest of the emulsion
7. 7
   workup.ADDITIONhalf of the monomer emulsion had been added to the reactor
8. 8
   درجة الحرارةAlso at this time the reactor stirrer was increased to 350 RPM
9. 9
   workup.ADDITIONOnce all the monomer emulsion was charged into the main reactor
10. 10
    workup.WAITthe temperature was held at 80° C. for an additional 2 hours
11. 11
    أخرىthe reaction
12. 12
    درجة الحرارةFull cooling
13. 13
    أخرىwas reduced to 35° C
14. 14
    أخرىThe product was collected into a holding tank
15. 15
    أخرىAfter drying the latex the molecular properties

الإجراء التجريبي

Separately the monomer emulsion was prepared in the following manner. 323 kg of styrene, 83 kg of butyl acrylate and 12.21 kg of β-CEA, 2.85 kg of 1-dodecanethiol, 1.42 kg of ADOD, 8.04 kg of Dowfax 2A1 (anionic surfactant), and 193 kg of deionized water were mixed to form an emulsion. 1% of the above emulsion was then slowly fed into the reactor containing the aqueous surfactant phase at 80° C. to form the “seeds” while being purged with nitrogen. The initiator solution was then slowly charged into the reactor and after 10 minutes the rest of the emulsion was continuously fed using a metering pump at a rate of 0.5%/min. After 100 minutes, half of the monomer emulsion had been added to the reactor. At this time, 3.42 kilograms of 1-dodecanethiol was stirred into the monomer emulsion, and the emulsion was continuously fed in at a rate of 0.5%/min. Also at this time the reactor stirrer was increased to 350 RPM. Once all the monomer emulsion was charged into the main reactor, the temperature was held at 80° C. for an additional 2 hours to complete the reaction. Full cooling was then applied and the reactor temperature was reduced to 35° C. The product was collected into a holding tank. The particle size was calculated to be 180 nanometers. After drying the latex the molecular properties were Mw=37,500 Mn=10,900 g/mol and the onset Tg was 55.0° C.