تفاعل #162247

معادلة التفاعل

methyl methacrylate

V-601

methacrylic acid

V-601

V-601

isobornyl methacrylate

→

methyl methacrylate isobornyl methacrylate methacrylic acid

المذيبات

methyl ethyl ketone

methyl ethyl ketone

methyl ethyl ketone

methyl ethyl ketone

ظروف التفاعل

المعالجة

1. 1
   درجة الحرارةa thermometer, a reflux cooling tube, and a nitrogen gas-introducing tube
2. 2
   أخرىwas being kept at 75° C.
3. 3
   workup.ADDITIONwas added dropwise
4. 4
   workup.ADDITIONsuch that the dropwise addition
5. 5
   workup.ADDITIONAfter the dropwise addition
6. 6
   workup.ADDITIONwas added
7. 7
   workup.ADDITIONwas added
8. 8
   workup.STIRRINGby stirring for 2 hours at 75° C
9. 9
   درجة الحرارةThereafter, the temperature thereof was increased to 85° C.
10. 10
    workup.STIRRINGto continue stirring for 2 more hours

الإجراء التجريبي

540.0 g of methyl ethyl ketone was put in a 2 L three-neck flask including a mechanical stirrer, a thermometer, a reflux cooling tube, and a nitrogen gas-introducing tube, and the temperature thereof was increased to 75° C. While the internal pressure of the reaction container was being kept at 75° C., a mixed solution including 108 g of methyl methacrylate, 388.8 g of isobornyl methacrylate, 43.2 g of methacrylic acid, 108 g of methyl ethyl ketone, and 2.1 g of “V-601” (trade name, manufactured by Wako Pure Chemical Industries, Ltd.) was added dropwise thereto such that the dropwise addition was completed in 2 hours. After the dropwise addition ended, a solution including 1.15 g of “V-601” (described above) and 15.0 g of methyl ethyl ketone was added thereto, followed by stirring for 2 hours at 75° C. In addition, a solution including 0.54 g of “V-601” (described above) and 15.0 g of methyl ethyl ketone was added thereto, followed by stirring for 2 hours at 75° C. Thereafter, the temperature thereof was increased to 85° C. to continue stirring for 2 more hours, thereby obtaining a resin solution of a methyl methacrylate/isobornyl methacrylate/methacrylic acid (=20/72/8 [mass ratio]) copolymer.