تفاعل #1538313

معادلة التفاعل

Vinyl pyrrolidone

vinyl caprolactam

dimethylaminopropyl methacrylamide

n-octadecyl methacrylate

→

DMAPMA n-Octadecyl Methacrylate

المذيبات

ethanol

ظروف التفاعل

المعالجة

1. 1
   أخرىThe reaction flask was equipped with a condenser
2. 2
   workup.ADDITIONa thermometer, a septum (for catalyst addition)
3. 3
   أخرىan anchor-type metal stirrer, and a nitrogen sparge tube
4. 4
   أخرىNitrogen was bubbled through the solution while the resin flask
5. 5
   أخرىAfter an additional half-hour of degassing
6. 6
   أخرىwere made at 10, 40, 70, 100, 140, 180 and 240 minutes
7. 7
   workup.ADDITIONafter the first addition
8. 8
   أخرىwas then brought up to 75° C.
9. 9
   درجة الحرارةcooled to room temperature

الإجراء التجريبي

Vinyl pyrrolidone (55.6 g), vinyl caprolactam (577.5 g), dimethylaminopropyl methacrylamide (DMAPMA) (42.6 g), n-octadecyl methacrylate (33.9 g) and ethanol (867.2 g) were charged into a 2-liter water-jacketed resin flask. The reaction flask was equipped with a condenser, a thermometer, a septum (for catalyst addition), an anchor-type metal stirrer, and a nitrogen sparge tube. Nitrogen was bubbled through the solution while the resin flask was heated to 68° C. using hot water circulating through the jacketed flask. After an additional half-hour of degassing at reflexing, a first shot of Lupersol 11 (0.25 ml) was injected into the flask. Subsequently, Lupersol 11 additions were made at 10, 40, 70, 100, 140, 180 and 240 minutes after the first addition. The reaction temperature was then brought up to 75° C. and held for an additional 5 hours, then cooled to room temperature and discharged.