تفاعل #1265345

معادلة التفاعل

iron oxide

potassium lactate

aluminum chloride

potassium lactate

sodium N-myristoyl-L-glutamate

sodium N-myristoyl-L-glutamate

zinc sulfate

→

aluminum N-myristoyl-L-glutamate

zinc lactate

iron oxide

المذيبات

water

water

water

ظروف التفاعل

المعالجة

1. 1
   workup.ADDITIONmixed
2. 2
   workup.ADDITIONuntil well dispersed
3. 3
   workup.ADDITIONthen added to the above mixture
4. 4
   workup.ADDITIONmixed for 10 minutes
5. 5
   workup.ADDITIONwas added dropwise
6. 6
   درجة الحرارةheated at 50° C.
7. 7
   workup.ADDITIONthen added to the above mixture
8. 8
   workup.ADDITIONmixed for 10 minutes
9. 9
   workup.STIRRINGWhile this was being stirred
10. 10
    workup.ADDITIONwas added dropwise
11. 11
    ترشيحThe product was filtered with suction
12. 12
    غسيلby rinsing with purified water
13. 13
    أخرىa temperature of 100° C.
14. 14
    أخرىThe cake was crushed
15. 15
    درجة الحرارةafter cooling

الإجراء التجريبي

One hundred grams of red iron oxide pigment was added to 500 ml of water and mixed using a home type mixer until well dispersed. Four grams of sodium N-myristoyl-L-glutamate having an HLB value of 4 was dissolved in 50 ml of water heated at 60° C. then added to the above mixture and mixed for 10 minutes. While this was being stirred, 2 chemical equivalents of aluminum chloride aqueous solution, based on the sodium N-myristoyl-L-glutamate, was added dropwise. Four grams of potassium lactate having an HLB value of 17 was dissolved in 50 ml of water heated at 50° C. then added to the above mixture and mixed for 10 minutes. While this was being stirred, 2 chemical equivalents of zinc sulfate aqueous solution, based on the potassium lactate, was added dropwise. The product was filtered with suction using a Buchner funnel, followed by rinsing with purified water. The filter cake was then baked in an oven for two hours after the filter cake reaches a temperature of 100° C. to further dehydrate the filter cake. The cake was crushed and pulverized to a powder after cooling. This resulted in a red iron oxide pigment chemically immobilized with aluminum N-myristoyl-L-glutamate and zinc lactate.

المصدر